Corrosion Behaviour of Steel/55% Al-Zn Alloy/Paint Systems Exposed to Natural and Artificial Environments
The corrosion performance of steel/55%Al–Zn alloy sheets pre‐treated with 5% Fe (NO3)3þ15% H3PO4 solution, and then coated with acrylic (AC), alkyd (AQ), vinyl (VL), solvent‐based epoxy (ES) or waterborne epoxy (EA) corrosion‐inhibiting primersþa barrier topcoat alkyd paint was studied. Exposure con...
Guardado en:
| Autores principales: | , , , |
|---|---|
| Formato: | Articulo |
| Lenguaje: | Inglés |
| Publicado: |
2014
|
| Materias: | |
| Acceso en línea: | http://sedici.unlp.edu.ar/handle/10915/81355 |
| Aporte de: |
| id |
I19-R120-10915-81355 |
|---|---|
| record_format |
dspace |
| institution |
Universidad Nacional de La Plata |
| institution_str |
I-19 |
| repository_str |
R-120 |
| collection |
SEDICI (UNLP) |
| language |
Inglés |
| topic |
Ingeniería Steel/55%Al–Zn Painting systems Adhesion Weathering Corrosion Blistering EIS |
| spellingShingle |
Ingeniería Steel/55%Al–Zn Painting systems Adhesion Weathering Corrosion Blistering EIS Elsner, Cecilia Inés Del Amo, Delia Beatriz Hernández, Luis S. Di Sarli, Alejandro Ramón Corrosion Behaviour of Steel/55% Al-Zn Alloy/Paint Systems Exposed to Natural and Artificial Environments |
| topic_facet |
Ingeniería Steel/55%Al–Zn Painting systems Adhesion Weathering Corrosion Blistering EIS |
| description |
The corrosion performance of steel/55%Al–Zn alloy sheets pre‐treated with 5% Fe (NO3)3þ15% H3PO4 solution, and then coated with acrylic (AC), alkyd (AQ), vinyl (VL), solvent‐based epoxy (ES) or waterborne epoxy (EA) corrosion‐inhibiting primersþa barrier topcoat alkyd paint was studied. Exposure conditions included weathering chambers and natural atmospheres (La Plata‐Argentina and San Luis‐Potosí, México). The panels' behaviour was evaluated through visual inspections and EIS measurements. Their results allowed inferring that: (1) most of the painting systems have a satisfactory performance during their exposure to the accelerated weathering chamber or the natural atmospheric stations and (2) the correlation between them allowed explaining some problems arising in service. This information will allow extending the useful life by adjusting the painting system formulation. |
| format |
Articulo Articulo |
| author |
Elsner, Cecilia Inés Del Amo, Delia Beatriz Hernández, Luis S. Di Sarli, Alejandro Ramón |
| author_facet |
Elsner, Cecilia Inés Del Amo, Delia Beatriz Hernández, Luis S. Di Sarli, Alejandro Ramón |
| author_sort |
Elsner, Cecilia Inés |
| title |
Corrosion Behaviour of Steel/55% Al-Zn Alloy/Paint Systems Exposed to Natural and Artificial Environments |
| title_short |
Corrosion Behaviour of Steel/55% Al-Zn Alloy/Paint Systems Exposed to Natural and Artificial Environments |
| title_full |
Corrosion Behaviour of Steel/55% Al-Zn Alloy/Paint Systems Exposed to Natural and Artificial Environments |
| title_fullStr |
Corrosion Behaviour of Steel/55% Al-Zn Alloy/Paint Systems Exposed to Natural and Artificial Environments |
| title_full_unstemmed |
Corrosion Behaviour of Steel/55% Al-Zn Alloy/Paint Systems Exposed to Natural and Artificial Environments |
| title_sort |
corrosion behaviour of steel/55% al-zn alloy/paint systems exposed to natural and artificial environments |
| publishDate |
2014 |
| url |
http://sedici.unlp.edu.ar/handle/10915/81355 |
| work_keys_str_mv |
AT elsnerceciliaines corrosionbehaviourofsteel55alznalloypaintsystemsexposedtonaturalandartificialenvironments AT delamodeliabeatriz corrosionbehaviourofsteel55alznalloypaintsystemsexposedtonaturalandartificialenvironments AT hernandezluiss corrosionbehaviourofsteel55alznalloypaintsystemsexposedtonaturalandartificialenvironments AT disarlialejandroramon corrosionbehaviourofsteel55alznalloypaintsystemsexposedtonaturalandartificialenvironments |
| bdutipo_str |
Repositorios |
| _version_ |
1764820488029208576 |