Efecto de la concentración del dopante sobre la estructura y la morfología en películas delgadas de Y2O3 - HfO2 y CaO - HfO2
Se depositaron películas delgadas de (Y2O3)x-Hf(1-2x)O2-x y (CaO)y-Hf(1-y)O2-y (x: 0.025, 0.1 y 0.12; y:0.06, 0.14 y 0.2) sobre sustratos de Al2O3 mediante la técnica de Dip-coating a partir de soluciones alcohólicas de organometálicos utilizando 3-hidroxi-2-butanona (Acetoín) como agente quelante....
| Autores principales: | , , , , |
|---|---|
| Formato: | Capítulo de libro |
| Lenguaje: | Español |
| Publicado: |
Villa Martelli, Buenos Aires :
Asociación Física Argentina,
2007
|
| Materias: | |
| Acceso en línea: | Registro en la Biblioteca Digital Handle |
| Aporte de: | Registro referencial: Solicitar el recurso aquí |
| LEADER | 04835naa a22005057a 4500 | ||
|---|---|---|---|
| 003 | AR-BaUEN | ||
| 005 | 20230809095141.0 | ||
| 008 | 220906s2007 ag ado|fo|||| 000 0 spa d | ||
| 022 | |a 1850-1168 | ||
| 040 | |a AR-BaUEN |b spa | ||
| 041 | 0 | |b spa |b eng | |
| 044 | |a ag | ||
| 100 | 1 | |4 aut |a Barolin, Sebastián Andrés |e autor |u Universidad Nacional de Rosario - CONICET. Instituto de Física de Rosario (IFIR). Santa Fe. Argentina | |
| 245 | 1 | 0 | |a Efecto de la concentración del dopante sobre la estructura y la morfología en películas delgadas de Y2O3 - HfO2 y CaO - HfO2 |
| 246 | 3 | 1 | |a Y2O3 - HfO2 and CaO - HfO2 thin films : |b effect of dopant concentration on the structure and morphology |
| 260 | |a Villa Martelli, Buenos Aires : |b Asociación Física Argentina, |c 2007 | ||
| 270 | |m oski@fceia.unr.edu.ar |z Correo electrónico del Autor de correspondencia | ||
| 300 | |a p. 174-176 : |b il., fotos, gráfs., tablas | ||
| 504 | |a Referencias bibliográficas. | ||
| 506 | |2 openaire |e Acuerdo editorial |f info:eu-repo/semantics/openAccess | ||
| 518 | |o Fecha de publicación en la Biblioteca Digital FCEN-UBA |d 2023-03-23 | ||
| 520 | 3 | |a Se depositaron películas delgadas de (Y2O3)x-Hf(1-2x)O2-x y (CaO)y-Hf(1-y)O2-y (x: 0.025, 0.1 y 0.12; y:0.06, 0.14 y 0.2) sobre sustratos de Al2O3 mediante la técnica de Dip-coating a partir de soluciones alcohólicas de organometálicos utilizando 3-hidroxi-2-butanona (Acetoín) como agente quelante. El quemado de los residuos orgánicos se realizó a 500 ºC bajo atmósfera normal. Las películas fueron tratadas térmicamente a intervalos de temperatura creciente hasta una temperatura máxima de 1250ºC. La morfología y el tamaño de grano de las películas se estudiaron mediante Microscopía de Fuerzas Atómicas (AFM) a temperatura ambiente. La evolución térmica de la estructura cristalina se monitoreó por ex-situ DRX en configuración φ-2θ con haz rasante y mediante análisis térmico DTG de polvos equivalentes. Concentraciones crecientes de ambos dopantes incrementan la temperatura de estabilidad de la fase metaestable cúbica, sin embargo para 1250 ºC, sólo la película (Y2O3)x-Hf(1-2x)O2-x no exhibe la presencia de fase monoclínica |l spa | |
| 520 | 3 | |a (Y2O3)x-Hf(1-2x)O2-x y (CaO)y-Hf(1-y)O2-y (x: 0.025, 0.1 y 0.12; y:0.06, 0.14 y 0.2) coatings were synthesized by Chemical Solution Deposition (CSD) from alcoholic solution using 3-hidroxi-2-butanone (Acetoín) as chelant agent. Burning of organic waste was carried out at 500 °C under normal atmosphere. Films were deposited onto alumina substrates by Dip Coating technique. The films were thermally treated at intervals of temperature rising to a maximum temperature of 1250° C. By means Atomic Force Microscopy (AFM) and Glazing Incidence X-ray Diffraction (φ-2θ configuration) morphology and phases evolution were studied. Increasing concentrations of both dopants increase temperature of the phase stability of cubic metaestable, but for 1250 °C, only the film (Y2O3) x-Hf (1-2x) O2-x did not exhibit the presence of monoclinic phase |l eng | |
| 540 | |2 cc |f https://creativecommons.org/licenses/by-nc-sa/2.5/ar | ||
| 653 | 1 | 0 | |a HFO2–Y2O3, HFO2–CAO |
| 653 | 1 | 0 | |a PELICULAS |
| 653 | 1 | 0 | |a EVOLUCION DE FASES |
| 690 | 1 | 0 | |a HFO2–Y2O3, HFO2–CAO |
| 690 | 1 | 0 | |a FILMS |
| 690 | 1 | 0 | |a PHASES EVOLUTION |
| 700 | 1 | |4 aut |a Giannone, María Laura |e autor |u Universidad Nacional de Rosario - CONICET. Instituto de Física de Rosario (IFIR). Santa Fe. Argentina | |
| 700 | 1 | |4 aut |a Balbi, Marcela Angela |e autor |u Universidad Nacional de Rosario - CONICET. Instituto de Física de Rosario (IFIR). Santa Fe. Argentina | |
| 700 | 1 | |4 aut |a Roldán, M. V. |e autor |u Universidad Nacional de Rosario - CONICET. Instituto de Física de Rosario (IFIR). Santa Fe. Argentina | |
| 700 | 1 | |4 aut |a Sanctis, Oscar Alberto de |e autor |g oski@fceia.unr.edu.ar |u Universidad Nacional de Rosario - CONICET. Instituto de Física de Rosario (IFIR). Santa Fe. Argentina | |
| 773 | 0 | |d Villa Martelli, Buenos Aires. Asociación Física Argentina, |g v. 19 |h pp. 174-176 |k n. 01 |p An. (Asoc. Fís. Argent., En línea) |w (AR-BaUEN)CENRE-9838 |x 1850-1168 |t Anales AFA | |
| 856 | 4 | 1 | |q application/pdf |u https://bibliotecadigital.exactas.uba.ar/collection/afa/document/afa_v19_n01_p174 |x registro |y Registro en la Biblioteca Digital |
| 856 | 4 | 1 | |q application/pdf |x derivado |y PDF |u https://bibliotecadigital.exactas.uba.ar/download/afa/afa_v19_n01_p174.pdf |
| 856 | 4 | 1 | |q application/pdf |u https://hdl.handle.net/20.500.12110/afa_v19_n01_p174 |x hdl |y Handle |
| 901 | |l 7 |m Rosana Benitez |n 7 |q Rosana Benitez | ||
| 942 | |c ASER |n 0 | ||
| 961 | |a afa_v19_n01_p174 |b afa |c PU |e ND | ||
| 962 | |a info:ar-repo/semantics/artículo |a info:eu-repo/semantics/article |b info:eu-repo/semantics/publishedVersion | ||
| 963 | |a AA | ||
| 976 | |a AEX | ||
| 999 | |c 90710 |d 90710 | ||